Scientific Reports volume 13, Article number: 16221 (2023) Cite this article

1468 Accesses

2 Altmetric

Metrics details

Due to the importance of energy storage systems based on supercapacitors, various studies have been conducted. In this research CuO, NCNO and the flower like CuO/NCNO have been studied as a novel materials in this field. The resulte showed that the synthesized CuO nanostructutes have flower like morphology which studied by FE-SEM analisis. Further, the XRD pattern confirmed the crystalline properties of the CuO/NCNO nanocomposite, and the Raman verified the functional groups and vibrations of the components of CuO/NCNO nanocomposite. In a two-electrode system at a current density of 4 A/g, the capacitance, power density, and energy density were 450 F/g, 3200 W/kg, and 98 Wh/kg, respectively. The charge transfer resistances of CuO and NCNO/CuO electrodes obtained 8 and 2 Ω respectively, which show that the conductivity and supercapacitive properties of nanocomposite are better than pure components. Also, the stability and low charge transfer resistance are other advantages obtained in a two-symmetrical electrode investigation. The stability investigation showed that after 3000 consecutive cycles, only 4% of the initial capacitance of the CuO/NCNO electrode decreased.

The use of energy storage devices such as batteries and conventional capacitors has been limited due to their large size, low power density, low capacitance, long times required for charging, short lifespan, and environmental pollution1,2,3,4,5,6,7,8,9. Introducing supercapacitors as developed electrochemical capacitors with excellent features including very high density, high speed of charging and discharging, high capacitance, and biocompatibility as well as their industry-scale application (electric vehicles, electrical installations, and the electricity support of factories) and so on have partially resolved the concerns created in the field of using energy storage devices10,11,12,13,14,15,16,17. Electrochemical supercapacitors have two mechanisms for charge storage depending on the type of materials used in the electrode structure. The charge storage mechanism at the electrode–electrolyte interface is due to the ion adsorption in an electric double-layer capacitor (EDLC)18,19. The EDLC electrochemical supercapacitors system mainly consists of carbon materials with high surface area and porous structures such as activated carbon, carbon nanotubes, and graphene20,21,22,23,24,25,26. In pseudo-capacitors, the charge storage mechanism is based on redox reactions or electron transfer (faradaic reactions). Conductive polymers, metals, and transition metal oxides are often used in their structure27,28,29,30,31. Carbon nanomaterials are the best materials in electrode for electrochemical supercapacitors owing to their easy accessibility, high chemical and mechanical stability, large surface area, and excellent electrical conductivity. Despite the abundant use of pure carbon nanomaterials in electrochemical fields, especially for energy storage, low capacitance, and energy density have limited their commercial use. Doping heteroatoms such as phosphorus (P), nitrogen (N), oxygen (O), sulfur (S), and fluorine (F) in the structure of the carbon matrix is one of the suitable modification approaches for improving the electrochemical properties and commercialization of carbon nanomaterials32,33,34. Nitrogen (N) heteroatom has been studied more than other heteroatoms due to the ease of integration in the structure of carbon nanomaterials, placement in the structure with different chemical forms, and creation of active sites for redox reactions. Also, N atoms, having high electronegativity compared to C and H atoms, induce a positive charge on the adjacent carbon atoms, which increases the active sites on the electrode surface to bind electrolyte ions and enhances electrode wettability35,36,37. Carbon nano onions (CNOs) are carbon particles containing multiple layers of graphene with SP2 hybridization38,39. The layered structure in CNOs spheres has caused the creation of many ion channels and pores, as well as increasing the accessibility of the outer surface of the structure, and these structural features increase its electrocatalytic activity40,41,42. Despite the good electrochemical activity and high charge–discharge rate, the capacitance and specific energy are low in CNOs structures43,44. A basic approach for raising the specific capacitance and the resistance of CNO structures is to dope N atoms in their structure, which can increase active surface centers for electrolyte ions adsorption on its surface, resulting in increased capacitance43,45. Based on the few provided reports on the application of N-doped CNOs structures, much effort is needed to improve these carbon structures’ application in the supercapacitors field46. Using transition metal oxides (TMOs) in the electrode structure increases reversible redox reactions, energy density, and capacitance47,48. Although using TMOs in the electrode structures (pseudo-capacitive electrodes) increases the specific capacitance, they can effectively reduce the energy density due to the limited potential window. The primary and practical solution is the nanocomposite fabricationby combining TMOs as pseudo-capacitor materials with carbon nanomaterials as EDLC materials and applying the metal oxide/carbon nanostructuresbased-nanocomposites as electrode materials in electrochemical supercapacitors49,50. The capacitors made by the mentioned nanocomposite materials are a hybrid of EDLC capacitors and pseudo-capacitors that have excellent properties of both types.

The formation of nanocomposite from carbon-based nanomaterials and TMOs is a suitable approach for improving the specific capacitance of CNOs and increasing its applications in electrochemical supercapacitors. Up to now, few studies have been reported on this area. Wang et al. reported Co3O4 /CNOs composite as electrochemical supercapacitor material51. The introduction of CNOs improved the structural stability and conductivity of Co3O4 electrode material. We designed CNOs/ MnO2/Fe3O4 nanocomposite as supercapacitor electrode materials52. Singh et al.53 used nanoporous gold (Au)–N doped CNOs-based micro-supercapacitor for developing an energy storage unit compatible with microelectronic devices. Due to favorable properties such as easy and fast synthesis, high abundance, excellent electrochemical and electrocatalytic properties, low toxicity, and variable morphology of nanoparticles, copper oxide (CuO) has been proposed as one of the widely used metal oxides in electrode materials for lithium-ion batteries, electrochemical capacitors and antibacterial54,55. Based on the latest information, no study has been done on making nanocomposite from the combination of CuO and N-CNOs and its application in hybrid electrochemical capacitors.

The properties of selected materials play a significant role in the capacitance of supercapacitors and current density, so choosing a suitable material for a supercapacitor is essential. Meanwhile, the type of morphology also causes many differences in the results. Choosing an environmentally friendly material with excellent ability as electrode material in a supercapacitor is necessary. Copper oxide is a good choice among metal oxides due to its reasonable price, good electrochemical properties, and environmental compatibility56. However, the electrochemical performance of copper oxide is still far from the amount required for practical applications due to its relatively low electrical conductivity. One of the ways to improve this problem is to use copper oxide-based nanocomposite with special morphology. Therefore, in this work, copper oxide with flower-like morphology is prepared57. This morphology prevents accumulation and aggregation in oxide nanoparticles and increases the electron transfer rate between the electrode and the electrolyte. In addition, considering the high surface area obtained from copper oxide in this morphology, more ions in electrolyte diffuse to the surface, resulting in the increased supercapacitor performance and properties of the oxide58,59,60. The surface area of copper oxide is improved by the presence of NCNO, which has good conductivity. Therefore, a new and desirable nanocomposite is prepared for designing a supercapacitor with high performance, increasing the stability of copper oxide in alkaline solutions, and bringing it closer to practical applications. According to the literature, CuO/NCNO nanocomposite with flower-like morphology has not been prepared so far. On the other hand, in this work, CuO/NCNO nanocomposite is synthesized directly on the nickel foam surface without using any polymer additives that affect the conductivity of the nanocomposite, as a result, both time and cost of consumables for supercapacitor preparation are saved. So, In this work, copper oxide nanoparticles were used to form a nanocomposite with N-doped CNO nanoparticles for use as electrode materials in electrochemical supercapacitors. The structure of NCNOs/CuO nanocomposite was characterized using SEM and XRD techniques. Cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and charge–discharge methods were used for the electrochemical analysis of the proposed nanocomposite-based supercapacitors.

Chitosan (Medium molecular weight, 98.0%), copper sulfate pentahydrate (99%), acetic acid (100%), potassium hydroxide (99%), hexamethylenetetramine (HMTA, 99%), were purchased from Merck company. The microstructure and distribution of elements of the catalysts were investigated by Field Emission Scanning Electron Microscopy (FE-SEM, TESCAN MIRA 3) outfitted with an energy dispersive spectrometer (EDS). X-ray diffraction (XRD) patterns were recorded using a Bruker D8 Advance diffractometer with Cu Kα radiation.

NCNO was prepared from a low-price material without using hazardous materials. For this purpose, 1 g of chitosan was mixed with 10% acetic acid at a temperature of 60 °C under stirring. Then 1 g of chitosan gel was mixed with 25 mL of water and introdused into the autoclave and put in an oven at 180 °C for 8 h. Finally, after the autoclave cooled down, the black product was washed with water and ethanol and dried at 60 °C.

The hydrothermal method was used to synthesize of flower-like CuO. For this mean, 1 g of copper sulfate was dissolved in 50 ml of water and stirred for 30 min. Also, 2 gr of HMTA was dissolved in 25 mL of water and added dropwise to the solution containing copper sulfate and stirred for 30 min. Afterward, the reaction mixture was transferred to an autoclave and heated at 180 °C for 10 h. After completing the reaction and cooling the product to ambient temperature, the flower-like CuO black product was separated by centrifuging, washing with water and ethanol, and dried at 60 °C for 12 h. The same method was used to synthesize the flower-like CuO/NCNO nanocomposite. During the pripartion of composite, 50 mg of NCNO was also exist in the solution. Also, after washing with acetone and water and drying at 60 °C for 12 h, nickel foam (1 × 1 cm) was placed in the autoclave, including nanocomposite precursors. After obtaining the final product, the nickel foam containing the product was washed with water and dried in an oven.

To obtain the specific capacitance (SC) of three- and two-electrode systems, Eqs. (1) and (2) are used, respectively. Also, Eqs. (3) and (4) are used to calculate power and energy density.

FE-SEM images of flower-like CuO and CuO/NCNO are shown in Fig. 1. As the FE-SEM images of copper oxide show, a flower-like morphology can be observed for this nanostructure. The same flower-like structure can be observed in the presence of NCNO spherical nanoparticles.

FE-SEM image of CuO and CuO/NCNO.

The XRD patterns of flower-like CuO and CuO/NCNO are shown in Fig. 2. The peaks observed at 2θ = 30.7, 36.9, 42.8, 43.7, 50.6, 61.6, 74.3, and 77 degrees are related to the (110), (002), (111), (− 200), (202), (− 113), (022) and (310) planes, respectively (according to JCPDS 0661-05) [95]. The same peaks can also be seen in the CuO/NCNO nanocomposite; however, the peak related to NCNO is not observed in the XRD pattern of the composite due to the low amounts of NCNO compared to CuO.

XRD pattrn of CuO and CuO/NCNO.

To additional approve the chemical composition of the prepared nanoostructures, X-ray photoelectron spectroscopy (XPS) analysis was executed. A measured spectrum of the CuO/NCNO nanocomposite is shown in Fig. 3a, which demonste that C, Cu and O elements are detected and no other impurity is present61. Three distinct aspects that represent three various chemical states in carbon may be extracted from the high-resolution C 1s peak of CNOs in Fig. 3b: The graphitic structure of C=C is responsible for the peak at 284.5 eV, whereas C–C bonds are responsible for the peak at 285.3 eV. Furthermore, C-O is associated with large peaks at 286.9 eV. Furthermore, the existence of C=O is blamed for the peak at 289.8 eV62. The high-resolution XPS spectrum of Cu 2p is shown in Fig. 3c. The peak positions of Cu 2p1/2 and Cu 2p3/2 were 953.8 eV and 933.8 eV, respectively. The fitted peaks at 934.5 eV and 954.7 eV are relevanted to CuO. In addition, the two detectable shake-up satellite peaks further indicate the existence of CuO63. The results are in good agreement with those of XRD, which further confirms the successful fabrication of CuO/NCNO composite.

(a) Survey XPS spectrum of CuO/NCNO, High-resolution XPS spectrum of (b) C1s and (c) Cu 2p from CuO/NCNO.

The Raman spectra of CuO, NCNO and CuO/NCNO are shown in Fig. 4. This figure shows two distinct peaks at 1350 and 1570 cm−1 for NCNO. The first peak at D band is related to structural defects, and the second peak at g band is related to E2g vibrations in aromatic carbons. Also, peaks related to CuO/NCNO can be seen in the Raman spectrum, which indicates the existence of NCNO in the CuO/NCNO nanocomposite. Other peaks observed in the Raman spectrum of CuO/NCNO nanocomposite correspond to those of the Raman spectrum of CuO. The observed peak is related to the monoclinic vibrations of the crystal structure, 291 cm−1, 337 cm−1, and 611 cm−1 are related to the A1g, \({B}_{g}^{1}\) and \({B}_{g}^{2}\), respectively.

Raman spectra of CuO, NCNO and CuO/NCNO.

TEM images of CuO, NCNO, and their nanocomposite are shown in Fig. 5. Tiny spherical nanoparticles are related to NCNO. Also, the images related to the flower-like CuO show the successful synthesis of this nanoparticle; the same morphology can be seen for CuO in the presence of NCNO.

TEM imge nanomaterials.

The supercapacitor behavior of CuO and CuO/NCNO nanocomposite in potassium hydroxide solution was investigated by CV in a potential range of − 0.2–0.65 V at a scan rate of 50 mV/s. The experiments were performed in a three-electrode system, including the reference electrode (saturated Ag/ AgCl), the counter electrode (platinum wire), and the working electrode (CuO and CuO/NCNO). The cyclic voltammograms of CuO and CuO/NCNO are shown in Fig. 6a. The cyclic voltammogram of the CuO electrode shows a pair of oxidation and reduction peaks that correspond to the conversion of copper (I) to copper (II) and vice versa, however, its current is not very high, so it is a quasi-reversible reaction. A better reversibility reaction with a higher oxidation and reduction current for CuO is observed when the flower-like copper oxide is formed in the presence of NCNO. Also, the surface area under a curve of CuO/NCNO electrode is greater than that of the CuO electrode due to the high surface area of NCNO, which results from a synergistic effect of CNO and CuO components. The oxidation and reduction current and surface area under the curve are more for this electrode. The shape of CV curve of CuO/NCNO electrode is more significant than that of the copper oxide electrode, indicating the higher capacitance of CuO/NCNO electrode than CuO electrode. As the cyclic voltammograms of the CuO/NCNO electrode show, the area under the CV curve is high, and an increase in the current (in the anodic and cathodic sections) is observed due to the 3D structure containing high-conductivity carbon nanomaterials. In fact, the synergistic effect between CuO nanoparticles and NCNO is quite evident; as a result, the increase in the capacitance of the CuO/NCNO electrode is observed. The electrochemical reaction that occurred on the CuO/NCNO electrode during the electrochemical process is suggested as follows:

(a) CV curves of CuO and CuO/NCNO in potassium hydroxide at scan rate 50 mV.s, (b) CV curves of CuO at differn scan rats, (c) CV curves of CuO/NCNO at differnt scan rats and (d) I versus υ1/2.

Cyclic voltammograms of CuO and CuO/NCNO electrodes at different scan rates are shown in Fig. 6b,c. According to these figures, the oxidation and reduction current increases gradually with increasing scan rate, indicating ideal capacitive behavior of this electrode. Also, shifting the anodic peaks and cathodic peaks toward the positive and the negative potentials, respectively, verify a quasi-reversible reaction for all the curves. The diagram of the current versus the square root of the scan rate is also displayed in Fig. 6d. There is a linear relationship between the oxidation peak currents and the square root of the scan rate for both CuO and CuO/NCNO electrodes, which shows that a quasi- reversible reaction has occurred on the surface of the electrode under the diffusion-controlled process. The voltammograms at various scan rates indicate that the Faraday current increases gradually as the scan rate increases, implying the ideal capacitive behavior of electrodes. Also, all cyclic voltammograms show a quasi-reversible process. As the voltammograms show, anodic peaks shift towards positive potentials, and cathodic peaks shift towards negative potentials as the scan rate increases, which is the main characteristic of pseudo-reversible reactions.

The specific capacitances of CuO/NCNO and CuO electrodes were investigated in a three-electrode system with potassium hydroxide solution as an electrolyte and chronopotentiometry method (Fig. 7). The charge/discharge curve was obtained in the potential range of -0.2 to 0.6 V and the current density of 1, 2, 3, and 4 A/g. As the current density decreases, the charge/discharge time becomes longer. Figure 7 shows the charge and discharge curves of CuO and CuO/NCNO electrodes. The obtained capacitances for the CuO at current densities of 1, 2, 3, and 4 A/g are 441.25, 367.5, 221.25, and 155 F/g; however, the capacitances values for CuO/NCNO electrodes at the mentioned current densities are 673.75, 572.5, 382.5 and 315 F/g, respectively. As it is known, the estimated specific capacitance decreases with increasing current density, which indicates that the electrode materials have little effect on electrochemical reactions.

charge and discharge curves of CuO and CuO/NCNO.

The EIS curves of the mentioned electrodes was obtained in a potassium hydroxide solution to check the resistance and conductivity of electrodes. The results are shown in Fig. 8. As the results also indicate, the charge transfer resistance of CuO/NCNO is lower than that of CuO electrode, which suggests that the electron transfer rate on the surface of this electrode is higher than that of the CuO electrode; therefore, the conductivity and capacitance of the electrode are higher. A comparison of the performance of the capacitive electrodes based on CuO and CuO/NCNO is reported in Table 1. The capacitance in this work is comparable and even superior than other electrodes due to the synergistic effect of CuO and NCNO. The CuO/NCNO capacitive electrode has a higher surface area and more active sites for the diffusion of the ions and Faraday reactions; therefore, better electrical conductivity is obtained at a more suitable charging time.

Nyquist plots of CuO and CuO/NCNO.

The greater electrochemical activity results from the synergistic impact of the double composite, which has high surface area providing more active sites, stronger electronic conductivity that offering fast charge transfer, and enhanced electrochemical performance of the CuO/NCNO electrode. Additionally, it is taken into account that the cyclic stability of electrode is a crucial element for practical applications.

The supercapacitor behavior of a symmetrical CuO/NCNO electrode system in a potassium hydroxide solution was investigated by the CV method. Cyclic voltammograms of the CuO/NCNO electrode in Fig. 9a show a pair of oxidation/reduction peaks that appears for this electrode, which is shifted by increasing the scan rate. In fact, a quasi-reversible behavior in the potential region of − 0.2–0.6 V is related to the oxidation/reduction reaction of copper with a favorable oxidation/reduction current in the presence of NCNO. Electrode capacitance, power, and energy density of CuO/NCNO electrode were investigated using chronopotentiometry method. The obtained capacitances for CuO/NCNO electrode in the current density of 1, 2, 3, and 4 A/g are 1072.5, 1015, 577.5, and 450 F/g, respectively (Fig. 9b). Also, the maximum power and energy density for this electrode are 98 W/kg and 3200 Wh/kg, at the current density of 1 and 4 A/g, respectively. The Ragone plot, Fig. 9c, shows that good quasi-capacitive behavior can be considered for this electrode due to the appropriate power and energy density. To study the stability of the CuO/NCNO electrode, 3000 consecutive charge/discharge cycles were recorded at a current density of 4 A/g. The results showed that the capacitance change of the CuO/NCNO electrode in the final cycle compared to the first cycle is 4%, so it can be conclude that the CuO/NCNO capacitive electrode has acceptable stability (Fig. 9d). Also, the charge transfer resistance in the potassium hydroxide solution based on the Nyquist diagram is 3 Ω indicating the excellent conductivity of this electrode (Fig. 10).

(a) CV curves of CuO/NCNO symmetrical system, (b) charge and discharge curves, (c) Ragone plot and (d) stability plot.

Nyquist plot of CuO and CuO/NCNO.

A supercapacitor electrode with suitable performance characteristics was prepared using flower-like NCNO and CuO. The conductivity of flower-like CuO electrode was improved due to the high surface area of CuO. This supercapacitor also provides a specific capacitance of 455 F/g (in a symmetrical system at 4 A/g) and a good stability after 3000 cycles. Therefore, the supercapacitor electrode obtained in this work as an energy storage device can provide acceptable results. The mentioned electrode is prepared without additives, and its preparation is more accessible than similar ones. As a result, it can be used as a low-cost, high-performance electrode in addition to the desirable supercapacitor characteristics.

The data used to support the findings of this study are available from the corresponding authors upon request.

Teymourinia, H. et al. GQDs/Sb2S3/TiO2 as a co-sensitized in DSSs: Improve the power conversion efficiency of DSSs through increasing light harvesting by using as-synthesized nanocomposite and mirror. Appl. Surf. Sci. 512, 145638 (2020).

Article CAS Google Scholar

Teymourinia, H., Salavati-Niasari, M., Amiri, O. & Farangi, M. Facile synthesis of graphene quantum dots from corn powder and their application as down conversion effect in quantum dot-dye-sensitized solar cell. J. Mol. Liq. 251, 267–272 (2018).

Article CAS Google Scholar

Naderi, L., Shahrokhian, S. & Soavi, F. Fabrication of a 2.8 V high-performance aqueous flexible fiber-shaped asymmetric micro-supercapacitor based on MnO2/PEDOT: PSS-reduced graphene oxide nanocomposite grown on carbon fiber electrode. J. Mater. Chem. A 8, 19588–19602 (2020).

Article CAS Google Scholar

Naderi, L. & Shahrokhian, S. Nickel vanadium sulfide grown on nickel copper phosphide Dendrites/Cu fibers for fabrication of all-solid-state wire-type micro-supercapacitors. Chem. Eng. J. 392, 124880 (2020).

Article CAS Google Scholar

Rajkumar, S., Subha, R., Gowri, S., Bella, A. & Merlin, J. P. Enhanced electrochemical performance of aminophenol-modified ZnO as electrode material for supercapacitors. Ionics https://doi.org/10.1007/s11581-021-04321-5 (2022).

Article Google Scholar

Portia, S., Srinivasan, R., Elaiyappillai, E., Johnson, P. M. & Ramamoorthy, K. Facile synthesis of Eu-doped CaTiO3 and their enhanced supercapacitive performance. Ionics 26, 3543–3554 (2020).

Article CAS Google Scholar

Angelin, M. D. et al. Electrochemical investigation of Zr-doped ZnO nanostructured electrode material for high-performance supercapacitor. Ionics 26, 5757–5772 (2020).

Article CAS Google Scholar

Xavier, A. R. et al. Synthesis and characterization of Sr-doped CdO nanoplatelets for supercapacitor applications. J. Mater. Sci. Mater. Electron. 33, 8426–8434 (2022).

Article CAS Google Scholar

Al-nayili, A. & Muhammad, N. J. Perovskite’s LaNiMnO6/montmorillonite K10 nanocomposites: Synthesis and enhanced photocatalytic activity. Mater. Sci. Semicond. Process. 155, 107254 (2023).

Article CAS Google Scholar

Winter, M. & Brodd, R. J. What are batteries, fuel cells, and supercapacitors?. Chem. Rev. 104, 4245–4270 (2004).

Article CAS PubMed Google Scholar

Miller, J. R. & Simon, P. Electrochemical capacitors for energy management. Science 321, 651–652 (2008).

Article CAS PubMed Google Scholar

Conway, B. E. Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications (Springer Science & Business Media, 2013).

Google Scholar

Shahrokhian, S., Naderi, L. & Mohammadi, R. High-performance fiber-shaped flexible asymmetric microsupercapacitor based on Ni(OH)2 nanoparticles-decorated porous dendritic Ni–Cu film/Cu wire and reduced graphene oxide/carbon fiber electrodes. ACS Sustain. Chem. Eng. 6, 14574–14588 (2018).

Article CAS Google Scholar

Alex, J. et al. Single step auto-igniting combustion technique grown CeO2 and Ni-doped CeO2 nanostructures for multifunctional applications. J. Alloys Compd. 882, 160409 (2021).

Article CAS Google Scholar

Srinivasan, R., Elaiyappillai, E., Nixon, E. J., Lydia, I. S. & Johnson, P. M. Enhanced electrochemical behaviour of Co-MOF/PANI composite electrode for supercapacitors. Inorg. Chim. Acta 502, 119393 (2020).

Article CAS Google Scholar

Angelin, M. D., Rajkumar, S., Ravichandran, A. & Merlin, J. P. Systematic investigation on the electrochemical performance of Cd-doped ZnO as electrode material for energy storage devices. J. Phys. Chem. Solids 161, 110486 (2022).

Article CAS Google Scholar

Al-Abidy, M. & Al-Nayili, A. Enhancement of photocatalytic activities of ZnFe2O4 composite by incorporating halloysite nanotubes for effective elimination of aqueous organic pollutants. Environ. Monit. Assess. 195, 190 (2023).

Article CAS Google Scholar

Chun, S.-E. et al. Design of aqueous redox-enhanced electrochemical capacitors with high specific energies and slow self-discharge. Nat. Commun. 6, 1–10 (2015).

Article Google Scholar

Al-Nayili, A. & Albdiry, M. Identification of active structure and catalytic efficiency of MCM-22 zeolite detemplated by two different processes. J. Porous Mater. 28, 1439–1448 (2021).

Article CAS Google Scholar

Cao, C. et al. Highly stretchable supercapacitors via crumpled vertically aligned carbon nanotube forests. Adv. Energy Mater. 9, 1900618 (2019).

Article Google Scholar

Zheng, C., Zhou, X., Cao, H., Wang, G. & Liu, Z. Synthesis of porous graphene/activated carbon composite with high packing density and large specific surface area for supercapacitor electrode material. J. Power Sour. 258, 290–296 (2014).

Article CAS ADS Google Scholar

Xu, G. et al. Binder-free activated carbon/carbon nanotube paper electrodes for use in supercapacitors. Nano Res. 4, 870–881 (2011).

Article CAS Google Scholar

Korkmaz, S. & Kariper, İA. Graphene and graphene oxide based aerogels: Synthesis, characteristics and supercapacitor applications. J. Energy Storage 27, 101038 (2020).

Article Google Scholar

Adib, K. et al. Sonochemical synthesis of Ag2WO4/RGO-based nanocomposite as a potential material for supercapacitors electrodes. Ceram. Int. 47, 14075–14086 (2021).

Article CAS Google Scholar

Ajel, M. K. & Al-Nayili, A. Synthesis, characterization of Ag-WO3/bentonite nanocomposites and their application in photocatalytic degradation of humic acid in water. Environ. Sci. Pollut. Res. https://doi.org/10.1007/s11356-022-23614-4 (2022).

Article Google Scholar

Alwan, S. H., Salem, K. H. & Alshamsi, H. A. Visible light-driven photocatalytic degradation of Rhodamine B dye onto TiO2/rGO nanocomposites. Mater. Today Commun. 33, 104558 (2022).

Article CAS Google Scholar

Mohammadnia, M. S. et al. Application of carbon nanoonion-NiMoO4-MnWO4 nanocomposite for modification of glassy carbon electrode: Electrochemical determination of ascorbic acid. Microchem. J. 159, 105470 (2020).

Article Google Scholar

Yue, T., Shen, B. & Gao, P. Carbon material/MnO2 as conductive skeleton for supercapacitor electrode material: A review. Renew. Sustain. Energy Rev. 158, 112131 (2022).

Article CAS Google Scholar

Li, N., Xiao, Y., Xu, C., Li, H. & Yang, X. Facile preparation of polyaniline nanoparticles via electrodeposition for supercapacitors. Int. J. Electrochem. Sci. 8, 1181–1188 (2013).

Article CAS Google Scholar

Albdiry, M. & Al-Nayili, A. Ternary sulfonated graphene/polyaniline/carbon nanotubes nanocomposites for high performance of supercapacitor electrodes. Polym. Bull. https://doi.org/10.1007/s00289-022-04495-6 (2022).

Article Google Scholar

Alwan, S. H. & Alshamsi, H. A. In situ synthesis NiO/F-MWCNTs nanocomposite for adsorption of malachite green dye from polluted water. Carbon Lett. 32, 1073–1084 (2022).

Article Google Scholar

Han, L.-N. et al. Nitrogen-doped carbon nets with micro/mesoporous structures as electrodes for high-performance supercapacitors. J. Mater. Chem. A 4, 16698–16705 (2016).

Article CAS Google Scholar

Batmunkh, M. et al. Sulfur-doped graphene with iron pyrite (FeS2) as an efficient and stable electrocatalyst for the iodine reduction reaction in dye-sensitized solar cells. Solar RRL 1, 1700011 (2017).

Article Google Scholar

Cai, Y. et al. Facile synthesis of three-dimensional heteroatom-doped and hierarchical egg-box-like carbons derived from moringa oleifera branches for high-performance supercapacitors. ACS Appl. Mater. Interfaces 8, 33060–33071 (2016).

Article CAS PubMed Google Scholar

Paraknowitsch, J. P. & Thomas, A. Doping carbons beyond nitrogen: an overview of advanced heteroatom doped carbons with boron, sulphur and phosphorus for energy applications. Energy Environ. Sci. 6, 2839–2855 (2013).

Article CAS Google Scholar

Li, X. et al. N, S co-doped 3D mesoporous carbon–Co3Si2O5(OH)4 architectures for high-performance flexible pseudo-solid-state supercapacitors. J. Mater. Chem. A 5, 12774–12781 (2017).

Article CAS Google Scholar

Sohouli, E., Shahdost-Fard, F., Rahimi-Nasrabadi, M., Plonska-Brzezinska, M. E. & Ahmadi, F. Introducing a novel nanocomposite consisting of nitrogen-doped carbon nano-onions and gold nanoparticles for the electrochemical sensor to measure acetaminophen. J. Electroanal. Chem. 871, 114309 (2020).

Article CAS Google Scholar

Mohapatra, D., Badrayyana, S. & Parida, S. Facile wick-and-oil flame synthesis of high-quality hydrophilic onion-like carbon nanoparticles. Mater. Chem. Phys. 174, 112–119 (2016).

Article CAS Google Scholar

Ghalkhani, M., Khosrowshahi, E. M. & Sohouli, E. Carbon Nano-Onions: Synthesis, Characterization, and Application 159–207 (Elsevier, 2021).

Google Scholar

Ghalkhani, M. & Sohouli, E. Synthesis of the decorated carbon nano onions with aminated MCM-41/Fe3O4 NPs: Morphology and electrochemical sensing performance for methotrexate analysis. Microporous Mesoporous Mater. 331, 111658 (2021).

Article Google Scholar

Sohouli, E. et al. A new electrochemical aptasensor based on gold/nitrogen-doped carbon nano-onions for the detection of Staphylococcus aureus. Electrochim. Acta 403, 139633 (2022).

Article CAS Google Scholar

Abdulhusain, Z. H., Alshamsi, H. A. & Salavati-Niasari, M. Silver and zinc oxide decorated on reduced graphene oxide: Simple synthesis of a ternary heterojunction nanocomposite as an effective visible-active photocatalyst. Int. J. Hydrog. Energy 47, 34036–34047 (2022).

Article CAS Google Scholar

Zheng, Y. et al. Sustainable nitrogen-doped carbon electrodes for use in high-performance supercapacitors and Li-ion capacitors. Sustain. Energy Fuels 4, 1789–1800 (2020).

Article CAS Google Scholar

N.S. Dayekh, A. Al-Nayili, Heterogeneous photocatalytic degradation of phenol over Pd/rGO sheets. In AIP Conference Proceedings 030010 (AIP Publishing LLC, 2022).

Pallavolu, M. R. et al. Design and synthesis of highly efficient Nitrogen-doped carbon nano-onions for asymmetric supercapacitors. J. Alloys Compd. 918, 165609 (2022).

Article CAS Google Scholar

Sohouli, E., Adib, K., Maddah, B. & Najafi, M. Manganese dioxide/cobalt tungstate/nitrogen-doped carbon nano-onions nanocomposite as new supercapacitor electrode. Ceram. Int. 48, 295–303 (2022).

Article CAS Google Scholar

Chandra Sekhar, S., Ramulu, B. & Yu, J. S. Transition Metal Oxides for Supercapacitors, Nanostructured Materials for Supercapacitors 267–292 (Springer, 2022).

Book Google Scholar

Al-nayili, A. & Rzoqy, M. Local silica sand as a silica source in the synthesis of Y zeolite. Asia-Pac. J. Chem. Eng. 17, e2824 (2022).

Article CAS Google Scholar

Kumar, A., Rathore, H. K., Sarkar, D. & Shukla, A. Nanoarchitectured transition metal oxides and their composites for supercapacitors. Electrochem. Sci. Adv. 6, e2100187 (2021).

Google Scholar

Huang, A. et al. Facile fabrication of multivalent VOx/graphene nanocomposite electrodes for high-energy-density symmetric supercapacitors. Adv. Energy Mater. 11, 2100768 (2021).

Article CAS Google Scholar

Wang, C. et al. Co3O4/carbon nano-onions composite as supercapacitor electrode and its excellent electrochemical performance. Int. J. Mater. Res. 109, 873–879 (2018).

Article CAS Google Scholar

Sohouli, E., Adib, K., Maddah, B. & Najafi, M. Preparation of a supercapacitor electrode based on carbon nano-onions/manganese dioxide/iron oxide nanocomposite. J. Energy Storage 52, 104987 (2022).

Article Google Scholar

Singh, B. K., Shaikh, A., Dusane, R. O. & Parida, S. Nanoporous gold–nitrogen–doped carbon nano-onions all-solid-state micro-supercapacitor. Nano-Struct. Nano-Objects 17, 239–247 (2019).

Article Google Scholar

Zaidan, B. A. H., Sohouli, E. & Mazaheri, S. A novel capping agent in preparation and characterization of CuAl2O4/CuO nanocomposite and its application for electrochemical detection of dopamine. Anal. Bioanal. Electrochem. 11, 108–122 (2019).

Google Scholar

Gbair, G. A. & Alshamsi, H. A. Facile green synthesis of CuO-ZnO nanocomposites from Argyreia nervosa leaves extract for photocatalytic degradation of Rhodamine B dye. Biomass Convers. Biorefin. https://doi.org/10.1007/s13399-022-03408-x (2022).

Article Google Scholar

Shinde, S. K., Dubal, D. P., Ghodake, G. S., Kim, D. Y. & Fulari, V. J. Morphological tuning of CuO nanostructures by simple preparative parameters in SILAR method and their consequent effect on supercapacitors. Nano-Struct. Nano-Objects 6, 5–13 (2016).

Article CAS Google Scholar

Chang, H.-W., Chen, S.-C., Chen, P.-W., Liu, F.-J. & Tsai, Y.-C. Constructing morphologically tunable copper oxide-based nanomaterials on cu wire with/without the deposition of manganese oxide as bifunctional materials for glucose sensing and supercapacitors. Int. J. Mol. Sci. 23, 3299 (2022).

Article CAS PubMed PubMed Central Google Scholar

Yu, Y. et al. Alkaline-carbonate-templated carbon: Effect of template nature on morphology, oxygen species and supercapacitor performances. Appl. Surf. Sci. 575, 151771 (2022).

Article CAS Google Scholar

Sadale, S. B., Patil, S. B., Teli, A. M., Masegi, H. & Noda, K. Effect of deposition potential and annealing on performance of electrodeposited copper oxide thin films for supercapacitor application. Solid State Sci. 123, 106780 (2022).

Article CAS Google Scholar

Teymourinia, H., Salavati-Niasari, M. & Amiri, O. Simple synthesis of Cu2O/GQDs nanocomposite with different morphologies fabricated by tuning the synthesis parameters as novel antibacterial material. Compos. Part B Eng. 172, 785–794 (2019).

Article CAS Google Scholar

Khan, M. A., Nayan, N., Ahmad, M. K. & Soon, C. F. Surface study of CuO nanopetals by advanced nanocharacterization techniques with enhanced optical and catalytic properties. Nanomaterials 10, 1298 (2020).

Article CAS PubMed PubMed Central Google Scholar

Tang, H. et al. Revealing the formation mechanism of ultrahard nanotwinned diamond from onion carbon. Carbon 129, 159–167 (2018).

Article CAS Google Scholar

Baig, N. & Saleh, T. A. Superhydrophobic polypropylene functionalized with nanoparticles for efficient fast static and dynamic separation of spilled oil from water. Glob. Chall. 3, 1800115 (2019).

Article PubMed PubMed Central Google Scholar

Wang, K., Dong, X., Zhao, C., Qian, X. & Xu, Y. Facile synthesis of Cu2O/CuO/RGO nanocomposite and its superior cyclability in supercapacitor. Electrochim. Acta 152, 433–442 (2015).

Article CAS Google Scholar

Eivazzadeh-Keihan, R. et al. Effective combination of rGO and CuO nanomaterials through poly (p-phenylenediamine) texture: Utilizing it as an excellent supercapacitor. Energy Fuels 35, 10869–10877 (2021).

Article CAS Google Scholar

Kamble, G. P. et al. CuCo2O4 nanorods coated with CuO nanoneedles for supercapacitor applications. ACS Appl. Nano Mater. 4, 12702–12711 (2021).

Article CAS Google Scholar

Lohar, G., Pore, O. & Fulari, A. Electrochemical behavior of CuO/rGO nanopellets for flexible supercapacitor, non-enzymatic glucose, and H2O2 sensing application. Ceram. Int. 47, 16674–16687 (2021).

Article CAS Google Scholar

Han, J. H., Kang, H. W. & Lee, W. Highly porous and capacitive copper oxide nanowire/graphene hybrid carbon nanostructure for high-performance supercapacitor electrodes. Compos. Part B Eng. 178, 107464 (2019).

Article Google Scholar

Subhash, K., Benoy, M., Siranjeevi, R. & Prabhu, S. Synthesis, and characterization of CuO/g-C3N4 nanocomposites for high performances supercapacitor application. Mater. Lett. 330, 133288 (2022).

Article Google Scholar

Download references

Department of Chemistry, Faculty of Science, University of Imam Hossein, Tehran, Iran

Esmail Sohouli & Koroush Adib

Department of Biotechnology, Research Institute of Modern Biological Techniques (RIMBT), University of Zanjan, Zanjan, 45371-38791, Iran

Hakimeh Teymourinia & Ali Ramazani

Department of Chemistry, Faculty of Science, University of Zanjan, Zanjan, 45371-38791, Iran

Hakimeh Teymourinia & Ali Ramazani

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Dr. E.S. acquired various electrochemical data and synthesized and characterized CuO and CuO/NCNO. Dr. H.T. and Dr. A.R. the Raman, XPS analysis, improve English language. Dr K.A., the supervisors of the project, provided all facilities and furthermore edited the manuscript. Also investigated the experimental data and reviewed and edited the manuscript.

Correspondence to Koroush Adib.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Sohouli, E., Teymourinia, H., Ramazani, A. et al. Preparation of high-performance supercapacitor electrode with nanocomposite of CuO/NCNO flower-like. Sci Rep 13, 16221 (2023). https://doi.org/10.1038/s41598-023-43430-1

Download citation

Received: 05 October 2022

Accepted: 23 September 2023

Published: 27 September 2023

DOI: https://doi.org/10.1038/s41598-023-43430-1

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.